Insulation Material For 10kV And Below Silane XLPE Aerial Cables - KABLO-10KV-VE-ALTI-SILAN-XLPE-ANTEN-KABLOLARI-ICIN-YALITIM-MALZEMESI
Description
Home / Cables / Wire and Cable
T/T, L/C, D/P, etc.
10 days
By Sea
Shanghai, China
3901909000
12 Months
The product is two-step silane cross-linkable polyethylene insulation compounds. It is mainly used for the insulation of medium-low voltage overhead cables through squeeze tube mold production process. Cables working voltage is 10kV and below, the highest working temperature is 90℃. The color of this product is black if there are no speical explanations.
Recommend to process with the PE extruder
No. Item Unit Technical Requirements 1 Density g/cm³ 0.922±0.005 2 Tensile Strength MPa ≥13.0 3 Elongation at Break % ≥300 4 Brittle Temperature with Low Temperature ℃ Failure Rate -76 ≤15/30 5 20℃ Volume Resist ivity Ω·m ≥1.0×10¹⁴ 6 20℃ Dielectric Strength,50Hz MV/m ≥25.0 7 20℃ Dielectric Constant,50Hz % ≤2.35 8 Air Aging Condition 135±2℃×168h Tensile Strength Variation After Aging % ±20 Elongation Variation After Aging % ±20 9 Artificial Weathering Aging Tensile Strength Variation After Aging % ±30 Elongation Variation After Aging % ±30 10 Artificial Weathering Aging Tensile Strength Variation After Aging % ±30 Elongation Variation After Aging % ±30 11 Hot Set Test Condition 200×0.2MPa×15min 1mm thick 95 ℃ boiled 2 hours test Hot Elongation % ≤100 Permanent Deformation after Cooling % ≤5 Note: More specifications, please contact our sales staff.
Specifications
Payment & Delivery
- Payment Terms:
- Delivery Time:
- Shipping:
- Port of Loading:
- HS Code:
- Storage:
Technical Table 1
| Model | Machine Barrel Temperature | Molding Temperature |
| OW-YJG(2)K-10 | 155-175℃ | 180-190℃ |
Technical Table 2
| No. | Item | Unit | Technical Requirements | ||
| 1 | Density | g/cm³ | 0.922±0.005 | ||
| 2 | Tensile Strength | MPa | ≥13.0 | ||
| 3 | Elongation at Break | % | ≥300 | ||
| 4 | Brittle Temperature with Low Temperature | ℃ Failure Rate | -76 ≤15/30 | ||
| 5 | 20℃ Volume Resist ivity | Ω·m | ≥1.0×10¹⁴ | ||
| 6 | 20℃ Dielectric Strength,50Hz | MV/m | ≥25.0 | ||
| 7 | 20℃ Dielectric Constant,50Hz | % | ≤2.35 | ||
| 8 | Air Aging Condition 135±2℃×168h | Tensile Strength Variation After Aging | % | ±20 | |
| Elongation Variation After Aging | % | ±20 | |||
| 9 | Artificial Weathering Aging | Tensile Strength Variation After Aging | % | ±30 | |
| Elongation Variation After Aging | % | ±30 | |||
| 10 | Artificial Weathering Aging | Tensile Strength Variation After Aging | % | ±30 | |
| Elongation Variation After Aging | % | ±30 | |||
| 11 | Hot Set Test Condition 200×0.2MPa×15min | 1mm thick 95 ℃ boiled 2 hours test | Hot Elongation | % | ≤100 |
| Permanent Deformation after Cooling | % | ≤5 | |||
| Note: More specifications, please contact our sales staff. | |||||