70℃ Lead-free Flame Retardant Sheath Compound
Description
Home / Cables / Wire and Cable
OW-(WZ)H-70 is granular compounds which is manufactured through mixing, plasticizing and pelletizing processes. It regards advanced PVC resin as basic raw materials, and add plasticizer, stabilizer, flame retardant and other accessory ingredients. It has good mechanical and physical property, electrical property and excellent processing performance. It meets RoHS Standard.
It is usually used for the sheath of 450/750V and below flame retardant cables.
Recommend to use single-screw extruders with L/D=20-25.
Specifications
Payment & Delivery
- Payment Terms:
- T/T, L/C, D/P, etc.
- Delivery Time:
- 10 days
- Shipping:
- By Sea
- Port of Loading:
- Shanghai, China
- HS Code:
- 3901909000
- Storage:
- 12 Months
Technical Table 1
| Model | Machine Barrel Temperature | Molding Temperature |
| OW-(WZ)H-70 | 145-165℃ | 165-175℃ |
Technical Table 2
| No. | Item | Unit | Technical Requirements |
| 1 | Oxygen Index | % | ≥30 |
| 2 | Tensile Strength | MPa | ≥15.0 |
| 3 | Elongation at Break | % | ≥180 |
| 4 | Thermal Deformation | % | ≤50 |
| 5 | Brittle Temperature With Low Temperature Impact | ℃ | -20 |
| 6 | 200℃ Thermal Stability | min | ≥50 |
| 7 | 20℃ Volume Resistivity | Ω·m | ≥1.0×10⁸ |
| 8 | Dielectric Strength | MV/m | ≥18 |
| 9 | Thermal Aging | \ | 100±2℃×168h |
| 10 | Dielectric Tensile Strength After Aging | MPa | ≥15.0 |
| 11 | Tensile Strength Variation | % | ±20 |
| 12 | Elongation After Aging | % | ≥180 |
| 13 | Elongation Variation | % | ±20 |
| 14 | Mass Losses (100℃×168h) | g/m² | ≤23 |
| 15 | HCL Gas Evolution | mg/g | ≤100 |
| 16 | Smoke Density – flame mode | Ds max | ≤300 |
| Note: More specifications, please contact our sales staff. | |||