Peroxide Crosslinkable Semi-Conductive Shielding Material For Conductor Of 10kV And Below XLPE Cables - KABLO-PEROKSIT-CAPRAZ-BAGLANABILIR-10KV-VE-ALTI-XLPE-KABLOLARIN-ILETKENLERI-ICIN-YARI-ILETKEN-KORUYUCU-MALZEME
Description
Home / Cables / Wire and Cable
T/T, L/C, D/P, etc.
10 days
By Sea
Shanghai, China
3901909000
12 Months
This product is applicable for conductor shielding of 10 kV and below XLPE insulated cables. It is produced with domestic raw materials by kneader equipment.
It has excellent mechanical and stable Processability performances.
Recommend to process with the PE extruder
Specifications
Payment & Delivery
- Payment Terms:
- Delivery Time:
- Shipping:
- Port of Loading:
- HS Code:
- Storage:
Technical Table 1
| Model | Machine Barrel Temperature | Molding Temperature |
| OW-YP(N)-10 | 70-110℃ | 110-118℃ |
Technical Table 2
| No | Item | Unit | Technical Requirements |
| 1 | Relative Density | g/cm³ | ≤1.20 |
| 2 | Tensile Strength | MPa | ≥14 |
| 3 | Elongation at Break | % | ≥200 |
| 4 | 20℃ Volume Resistivity | Ω·cm | ≤100 |
| 5 | 90℃ Volume Resistivity | Ω·cm | ≤1000 |
| 6 | 90℃ Volume Resistivity after air aging (100℃×168h) | Ω·cm | ≤1000 |
| 7 | Air Aging Test | / | (135±2℃)×168h |
| 8 | Tensile Strength Variation After Aging | % | ±25 |
| 9 | Elongation Variation After Aging | % | ±25 |
| 10 | Hot Set Test | / | 200℃×0.2MPa×15min |
| 11 | Hot Elongation | % | ≤100 |
| 12 | Permanent Deformation after Cooling (Set) | % | ≤15 |
| 13 | Peel Strength 20℃ | N/cm | – |
| 14 | Moisture Content | ppm | ≤900 |
| Note: More specfications, please contact our sales staff. | |||