Insulation Material For 3kV And Below Silane XLPE Cables - KABLO-3KV-VE-ALTI-SILAN-XLPE-KABLOLAR-ICIN-YALITIM-MALZEMESI
Description
Home / Cables / Wire and Cable
T/T, L/C, D/P, etc.
10 days
By Sea
Shanghai, China
3901909000
12 Months
Insulation Material for 3kV and below Silane XLPE Cables is two-step silane cross-linkable insulation compounds. It is mainly used for the insulation of low-voltage cables and control cables with working voltage for 3KV and below. The highest working temperature is 90℃.
It is suitable for squeeze tube mold production process.
Recommend to process with the PE extruder
No. Item Unit Technical Requirements 1 Density g/cm³ 0.922±0.005 2 Tensile Strength MPa ≥13.5 3 Elongation at Break % ≥350 4 Brittle Temperature with Low Temperature ℃ Failure Rate -76 ≤15/30 5 20℃ Volume Resistivity Ω·m ≥1.0×10¹⁴ 6 20C Dielectric Strength,50Hz MV/m ≥25.0 7 20℃ Dielectric Constant,50Hz – ≤2.35 8 Air Aging Condition 135±2℃×168h Tensile Strength Variation After Aging % ±20 Elongation Variation After Aging % ±20 9 Hot Set Test Condition 200℃×0.2MPa×15min 1mm thick 95 ℃ boiled 2 hours test Hot Elongation % ≤100 Permanent Deformation after Cooling % ≤5 Note: More speclfications, please contact our sales staff.
Specifications
Payment & Delivery
- Payment Terms:
- Delivery Time:
- Shipping:
- Port of Loading:
- HS Code:
- Storage:
Technical Table 1
| Model | Machine Barrel Temperature | Molding Temperature |
| OW-YJG (2)-3 | 155-175℃ | 180-190℃ |
Technical Table 2
| No. | Item | Unit | Technical Requirements | ||
| 1 | Density | g/cm³ | 0.922±0.005 | ||
| 2 | Tensile Strength | MPa | ≥13.5 | ||
| 3 | Elongation at Break | % | ≥350 | ||
| 4 | Brittle Temperature with Low Temperature | ℃ Failure Rate | -76 ≤15/30 | ||
| 5 | 20℃ Volume Resistivity | Ω·m | ≥1.0×10¹⁴ | ||
| 6 | 20C Dielectric Strength,50Hz | MV/m | ≥25.0 | ||
| 7 | 20℃ Dielectric Constant,50Hz | – | ≤2.35 | ||
| 8 | Air Aging Condition 135±2℃×168h | Tensile Strength Variation After Aging | % | ±20 | |
| Elongation Variation After Aging | % | ±20 | |||
| 9 | Hot Set Test Condition 200℃×0.2MPa×15min | 1mm thick 95 ℃ boiled 2 hours test | Hot Elongation | % | ≤100 |
| Permanent Deformation after Cooling | % | ≤5 | |||
| Note: More speclfications, please contact our sales staff. | |||||