Poly Butylene Terephthalate (PBT) - KABLO-POLI-BUTILEN-TEREFTALAT-PBT

Poly Butylene Terephthalate (PBT) - KABLO-POLI-BUTILEN-TEREFTALAT-PBT

Part Number: KABLO-POLI-BUTILEN-TEREFTALAT-PBT

Alternative Cross Numbers: 3907991090

Category: Cable Raw Materials

Description

Home / Cables / Fiber Optic Cable

30000t/y

T/T, L/C, D/P, etc.

3 days

18t / 20GP, 24t / 40GP

By sea

Shanghai, China

3907991090

6-8 months

Poly butylene Terephthalate is milky white or milky yellow translucent to opaque thermoplastic polyester particles. Poly butylene Terephthalate (PBT) has excellent mechanical properties, electrical insulation properties, oil resistance, chemical corrosion resistance, easy moulding and low moisture absorption, etc., and is the most commonly used material for optical fiber secondary coating.

In the optical fiber cable, the optical fiber is very fragile. Although the mechanical strength of the optical fiber is improved after the primary coating, the requirements for cabling are still not enough, so the secondary coating is required. The secondary coating is the most important mechanical protection method for the optical fiber in the optical fiber cable manufacturing process, because secondary coating not only provides further mechanical protection against compression and tension, but also creates excess length of optical fiber. Due to its good physical and chemical properties, Poly butylene terephthalate is usually used as an extrusion material for the secondary coating of optical fibers in outdoor optical fiber cable.

We can provide OW-6013,OW-6015 and other types of Poly butylene Terephthalate material for secondary coating of optical fiber cable.

The material PBT we provided has the following characteristics:
1) Good stability. Small shrinkage scale, small volume changing in using, good stability in forming.
2) High mechanical strength. Large modulus, good extension performance, high tensile strength. The anti-lateral pressure value of tube is higher than the standard.
3) High distortion temperature. Excellent distortion performance under large load and small load conditions.
4) Hydrolysis resistance. With excellent resistance to hydrolysis, making optical fiber cable more longer life than standard requirements.
5) Chemical resistance. Excellent chemical resistance and good compatibility with fiber paste and cable paste, not easy to be corroded.

Mainly used for the secondary coating production of the optical fiber of the outdoor loose-tube optical fiber cable.

Material PBT is packaged in 1000kg or 900kg polypropylene woven bag outer packing, lined with aluminum foil bag; or 25kg kraft paper bag outer packing, lined with aluminum foil bag.
After packaging, it is placed on a pallet.
1) 900kg ton bag size: 1.1m*1.1m*2.2m
2) 1000kg ton bag size: 1.1m*1.1m*2.3m

1) The product should be kept in a clean, hygienic, dry and ventilated storehouse.
2) The product should be kept away from chemicals and corrosive substances, should not be stacked together with flammable products and should not be close to fire sources.
3) The product should avoid direct sunlight and rain.
4) The product should be packed completely to avoid moisture and pollution.
5) The storage period of the product at ordinary temperature is 12 months from the date of production.

Specifications

Payment & Delivery

PRODUCTION CAPACITY:
PAYMENT TERMS:
DELIVERY TIME:
CONTAINER LOADING:
SHIPPING:
PORT OF LOADING:
HS CODE:
STORAGE:

Technical Table 1

No.	Testing Item	Unit	Standard Requirement	Value
1	Density	g/cm³	1.25～1.35	1.31
2	Melt flow rate (250℃、2160g)	g/10min	7.0～15.0	12.5
3	Moisture content	％	≤0.05	0.03
4	Water absorption	%	≤0.5	0.3
5	Tensile strength at yield	MPa	≥50	52.5
	Elongation at yield	%	4.0～10.0	4.4
	Breaking Elongation	%	≥100	326.5
	Tensile Modulus of elasticity	MPa	≥2100	2241
6	Flexural Modulus	MPa	≥2200	2243
6	Flexural Strength	MPa	≥60	76.1
7	Melting point	℃	210～240	216
8	Shore Hardness (HD)	/	≥70	73
9	Izod impact(23℃)	kJ/㎡	≥5.0	9.7
9	Izod impact(-40℃)	kJ/㎡	≥4.0	7.7
10	Coefficient of Linear Expansion (23℃～80℃)	10^-4K^-1	≤1.5	1.4
11	Volume resistivity	Ω·cm	≥1.0×10¹⁴	3.1×10¹⁶
12	Heat distortion temperature (1.80MPa)	℃	≥55	58
12	Heat distortion temperature (0.45MPa)	℃	≥170	178
13	Thermal hydrolysis
	Tensile Strength at Yield	MPa	≥50	51
	Elongation at Break	％	≥10	100
14	Compatibility between material and filling compounds
	Tensile Strength at Yield	MPa	≥50	51.8
	Elongation at Break	％	≥100	139.4
15	Loose tube anti side pressure	N	≥800	825
Note: This type of Poly butylene Terephthalate (PBT) is a general-purpose optical cable secondary coating material.

Technical Table 2

No.	Testing Item	Unit	Standard Requirement	Value
1	Density	g/cm³	1.25～1.35	1.31
2	Melt flow rate (250℃、2160g)	g/10min	7.0～15.0	12.6
3	Moisture content	％	≤0.05	0.03
4	Water absorption	%	≤0.5	0.3
5	Tensile strength at yield	MPa	≥50	55.1
	Elongation at yield	%	4.0～10.0	5.2
	Elongation at break	%	≥100	163
	Tensile Modulus of elasticity	MPa	≥2100	2316
6	Flexural Modulus	MPa	≥2200	2311
6	Flexural Strength	MPa	≥60	76.7
7	Melting point	℃	210～240	218
8	Shore Hardness (HD)	/	≥70	75
9	Izod impact (23℃)	kJ/㎡	≥5.0	9.4
9	Izod impact (-40℃)	kJ/㎡	≥4.0	7.6
10	Coefficient of Linear Expansion (23℃～80℃)	10^-4K^-1	≤1.5	1.44
11	Volume resistivity	Ω·cm	≥1.0×10¹⁴	4.3×10¹⁶
12	Heat distortion temperature (1.80MPa)	℃	≥55	58
12	Heat distortion temperature (0.45MPa)	℃	≥170	174
13	Thermal hydrolysis
	Tensile Strength at Yield	MPa	≥50	54.8
	Elongation at Break	％	≥10	48
14	Compatibility between material and filling compounds
	Tensile Strength at Yield	MPa	≥50	54.7
	Elongation at Break	％	≥100	148
15	Loose tube anti side pressure	N	≥800	983
Note: This Poly butylene Terephthalate (PBT) has high pressure resistance, and is suitable for the production of secondary coating of air-blown micro-optical cable.